Dynamic strain aging (DSA) for materials science is an instability in

plastic flow In engineering, deformation refers to the change in size or shape of an object. ''Displacements'' are the ''absolute'' change in position of a point on the object. Deflection is the relative change in external displacements on an object. Strain ...

of materials, associated with interaction between moving dislocations and diffusing solutes. Although sometimes dynamic strain aging is used interchangeably with the

Portevin–Le Chatelier effect The Portevin–Le Chatelier (PLC) effect describes a serrated stress–strain curve or jerky flow, which some materials exhibit as they undergo plastic deformation, specifically inhomogeneous deformation. This effect has been long associated wit ...

(or serrated yielding), dynamic strain aging refers specifically to the microscopic mechanism that induces the Portevin–Le Chatelier effect. This strengthening mechanism is related to solid-solution strengthening and has been observed in a variety of fcc and bcc substitutional and interstitial alloys, metalloids like silicon, and ordered intermetallics within specific ranges of temperature and strain rate.Mesarovic, Sinisa (1995)"Dynamic Strain Aging and Plastic Instabilities." J. Mech. Phys. Solids 43:671–701 No. 5

Description of mechanism

In materials, the motion of

dislocation In materials science, a dislocation or Taylor's dislocation is a linear crystallographic defect or irregularity within a crystal structure that contains an abrupt change in the arrangement of atoms. The movement of dislocations allow atoms to sl ...

s is a discontinuous process. When dislocations meet obstacles during plastic deformation (such as particles or forest dislocations), they are temporarily arrested for a certain time. During this time, solutes (such as interstitial particles or substitutional impurities) diffuse around the pinned dislocations, further strengthening the obstacles' hold on the dislocations. Eventually these dislocations will overcome the obstacles with sufficient stress and will quickly move to the next obstacle where they are stopped and the process can repeat.Van Den Beukel, A. (1975)"Theory of the Effect of Dynamic Strain Aging on Mechanical Properties". Phys. Stat. Sol. (a) 30 197: This process's most well-known macroscopic manifestations are Lüders bands and the Portevin–Le Chatelier effect. However, the mechanism is known to affect materials without these physical observations.Atkinson, JD and Yu, J.(1997) "The Role of Dynamic Strain-Aging in the Environment Assisted Cracking observed in Pressure Vessel Steels". Fatigue Fracture Eng. Mater. Struct. Vol.20 No. 1:1–12

Model for substitutional solute DSA

In metal alloys with substitutional solute elements, such as aluminum-magnesium alloys, dynamic strain aging leads to negative strain rate sensitivity which causes instability in plastic flow.Aboulfadi, H., Deges, J., Choi, P., Raabe, D. (2015) "Dynamic strain aging studied at the atomic scale," Acta Materialia 86:34-42 The

diffusion Diffusion is the net movement of anything (for example, atoms, ions, molecules, energy) generally from a region of higher concentration to a region of lower concentration. Diffusion is driven by a gradient in Gibbs free energy or chemical p ...

of solute elements around a dislocation can be modeled based on the energy required to move a solute atom across the slip plane of the dislocation.Curtin, W.A., Olmsted, D.L., Hector Jr., L.G. (2006) "A predictive mechanism for dynamic strain ageing in aluminium-magnesium alloys," Nature Materials 5:875-880 An edge dislocation produces a stress field which is compressive above the slip plane and tensile below.Cai, W., Nix, W.D. (2016) "Imperfections in Crystalline Solids," Cambridge University Press, In Al-Mg alloys, the Mg atom is larger than an Al atom and has lower energy on the tension side of the dislocation slip plane; therefore, Mg atoms in the vicinity of an edge dislocation are driven to diffuse across the slip plane (see figure). The resulting region of lower solute concentration above the slip plane weakens the material in the region near the pinned dislocation, such that when the dislocation becomes mobile again, the stress required to move it is temporarily reduced. This effect can manifest as serrations in the stress-strain curve (Portevin-Le Chatelier effect). Solute dislocation diffusion schematic

Because solute diffusion is thermally activated, increases in temperature can increase the rate and range of diffusion around a dislocation core. This can result in more severe stress drops, typically marked by a transition from Type A to Type C serrations.Pink, E., Grinberg, A. (1981) "Serrated flow in a ferritic stainless steel," Materials Science and Engineering 51 iss. 1, p.1-8

Material property effects

Although serrations in the

stress–strain curve In engineering and materials science, a stress–strain curve for a material gives the relationship between stress and strain. It is obtained by gradually applying load to a test coupon and measuring the deformation, from which the stress and ...

caused by the Portevin–Le Chatelier effect are the most visible effect of dynamic strain aging, other effects may be present when this effect is not seen. Often when serrated flow is not seen, dynamic strain aging is marked by a lower strain rate sensitivity. That becomes negative in the Portevin–Le Chatelier regime. Dynamic strain aging also causes a plateau in the strength, a peak in flow stress a peak in

work hardening In materials science, work hardening, also known as strain hardening, is the strengthening of a metal or polymer by plastic deformation. Work hardening may be desirable, undesirable, or inconsequential, depending on the context. This strengt ...

, a peak in the Hall–Petch constant, and minimum variation of

ductility Ductility is a mechanical property commonly described as a material's amenability to drawing (e.g. into wire). In materials science, ductility is defined by the degree to which a material can sustain plastic deformation under tensile stres ...

with temperature.Samuel, K.G, Mannan, S.L, Rodriguez, P (1996) "Another Manifestation of Dynamic Strain Ageing" Journal of Materials Science Letters 15:1697-1699 Since dynamic strain aging is a hardening phenomenon it increases the strength of the material.

Effect of alloying elements on DSA

Two categories can be distinguished by the interaction pathway. The first class of Elements, such as carbon(C) and nitrogen(N), contribute to DSA directly by diffusing quickly enough through the lattice to the dislocations and locking them. Such effect is determined with the element’s solubility, diffusion coefficient, and the interaction energy between the elements and dislocations, i.e. the severity of dislocation locking.

Types of DSA Serrations

At least five classes can be identified according to the stress-strain relation appearance of Serration.

Type A

Arising from the repeated nucleation of shear bands and the continuous propagation of Lüders bands, this type consists of periodic locking serrations with abrupt increase in flow stress followed by drop of stress below the general level of the stress-strain curve. It is usually seen in the low temperature (high strain rate) part of the DS regime.

Type B

Result from the nucleation of narrow shear bands, which propagate discontinuously or do not propagate due to the adjacent nucleation sites, and thus oscillate about the general level of the flow curve. It occurs at higher temperature or lower strain rates than type A. It may also be developed from type A when it comes to higher strain.

Type C

Caused by dislocation unlocking, the stress drop of type C is below the general level of the flow curve. It occurs at even higher temperature and lower strain comparation to A and B type.

Type D

When there is no work hardening, a plateau on the stress-strain curve is seen and therefore is also named staircase type. This type forms a mixed mode with type B.

Type E

Occurring at higher strain after type A, type E is not easy to be recognized.

Material specific example of dynamic strain aging

Dynamic strain aging has been shown to be linked to these specific material problems: *Decrease the fracture resistance of Al–Li alloys. *Decrease

low cycle fatigue Low cycle fatigue (LCF) has two fundamental characteristics: plastic deformation in each cycle; and low cycle phenomenon, in which the materials have finite endurance for this type of load. The term ''cycle'' refers to repeated applications of stres ...

life of austenitic stainless steels and super-alloys under test conditions which are similar to the service conditions in liquid-metal-cooled fast breeder reactors in which the material is used. *Reduce fracture toughness by 30–40% and shorten the air fatigue life of RPC steels and may worsen the cracking resistance of steels in aggressive environments. The susceptibility of RPC steels to environment assisted creating in high temperature water coincides with DSA behavior *PLC specific problems like blue brittleness in steel, loss of ductility and bad surface finishes for formed Aluminum Magnesium alloys.