Plaster mold casting is a

metalworking Metalworking is the process of shaping and reshaping metals to create useful objects, parts, assemblies, and large scale structures. As a term it covers a wide and diverse range of processes, skills, and tools for producing objects on every scale ...

casting Casting is a manufacturing process in which a liquid material is usually poured into a mold, which contains a hollow cavity of the desired shape, and then allowed to solidify. The solidified part is also known as a ''casting'', which is ejecte ...

process similar to

sand casting Sand casting, also known as sand molded casting, is a metal casting process characterized by using sand as the mold material. The term "sand casting" can also refer to an object produced via the sand casting process. Sand castings are produced ...

except the molding material is

plaster of Paris Plaster is a building material used for the protective or decorative coating of walls and ceilings and for moulding and casting decorative elements. In English, "plaster" usually means a material used for the interiors of buildings, while "re ...

instead of

sand Sand is a granular material composed of finely divided mineral particles. Sand has various compositions but is defined by its grain size. Sand grains are smaller than gravel and coarser than silt. Sand can also refer to a textural class ...

. Like sand casting, plaster mold casting is an expendable mold process, however it can only be used with non-ferrous materials. It is used for castings as small as to as large as . Generally, the form takes less than a week to prepare. Production rates of 1–10 units/hr can be achieved with plaster molds.. Parts that are typically made by plaster casting are lock components, gears, valves, fittings, tooling, and ornaments.

Details

The plaster is not pure plaster of Paris, but rather has additives to improve green strength, dry strength, permeability, and castability. For instance,

talc Talc, or talcum, is a clay mineral, composed of hydrated magnesium silicate with the chemical formula Mg3Si4O10(OH)2. Talc in powdered form, often combined with corn starch, is used as baby powder. This mineral is used as a thickening agent a ...

magnesium oxide Magnesium oxide ( Mg O), or magnesia, is a white hygroscopic solid mineral that occurs naturally as periclase and is a source of magnesium (see also oxide). It has an empirical formula of MgO and consists of a lattice of Mg2+ ions and O2� ...

are added to prevent cracking and reduce setting time; lime and

cement A cement is a binder, a chemical substance used for construction that sets, hardens, and adheres to other materials to bind them together. Cement is seldom used on its own, but rather to bind sand and gravel (aggregate) together. Cement mixe ...

limit expansion during baking; glass fibers increase strength; sand can be used as a filler. The ratio of ingredients is 70–80%

gypsum Gypsum is a soft sulfate mineral composed of calcium sulfate dihydrate, with the chemical formula . It is widely mined and is used as a fertilizer and as the main constituent in many forms of plaster, blackboard or sidewalk chalk, and drywa ...

and 20–30% additives.. The

pattern A pattern is a regularity in the world, in human-made design, or in abstract ideas. As such, the elements of a pattern repeat in a predictable manner. A geometric pattern is a kind of pattern formed of geometric shapes and typically repeated li ...

is usually made from metal, however

rubber Rubber, also called India rubber, latex, Amazonian rubber, ''caucho'', or ''caoutchouc'', as initially produced, consists of polymers of the organic compound isoprene, with minor impurities of other organic compounds. Thailand, Malaysia, and ...

molds may be used for complex geometry; these molds are called s. For example, if the casting includes

reentrant Reentrant or re-entrant can refer to: *Re-entrant (landform), the low ground formed between two hill spurs. *Reentrancy (computing) in computer programming * Reentrant mutex in computer science *Reentry (neural circuitry) in neuroscience * Salien ...

angles or complex angular surfaces then the rubber is flexible enough to be removed, unlike metal. These molds are also inexpensive, reusable, more accurate than steel molds, fast to produce, and easy to change. Typical tolerances are for the first and 0.02 mm per additional centimeter (0.002 in per additional inch). A draft of 0.5 to 1 degree is required. Standard

surface finish Surface finish, also known as surface texture or surface topography, is the nature of a surface as defined by the three characteristics of lay, surface roughness, and waviness.. It comprises the small, local deviations of a surface from the p ...

es that are attainable are 1.3 to 4 micrometers (50–125 μin).

Process

First, the parting line is determined - either simple two part or more complex (3 or more). A box is made around the pattern to hold the plaster. Then plaster is mixed and the pattern is sprayed with a thin film of parting compound also called a release agent to prevent the plaster from sticking to the pattern. The plaster is then poured over the pattern and the box holding the plaster and pattern is vibrated by mechanical means in order to fill all gaps and to release air bubbles. The plaster sets, usually in about 15 minutes, and the pattern is removed. The mold is then baked, between and , to remove any excess water. The dried mold is then assembled, preheated, and the metal poured. Finally, after the metal has solidified, the plaster is broken from the cast part. The mold is usually damaged from the metal so reusing is usually not done. Discarded plaster can be recycled by grinding but care must be used since silica dust causes lung damage.

Advantages and disadvantages

Plaster mold casting is used when an excellent surface finish and good dimensional accuracy is required. Because the plaster has a low

thermal conductivity The thermal conductivity of a material is a measure of its ability to conduct heat. It is commonly denoted by k, \lambda, or \kappa. Heat transfer occurs at a lower rate in materials of low thermal conductivity than in materials of high thermal ...

and

heat capacity Heat capacity or thermal capacity is a physical property of matter, defined as the amount of heat to be supplied to an object to produce a unit change in its temperature. The SI unit of heat capacity is joule per kelvin (J/K). Heat cap ...

, the metal cools more slowly than in a sand mold, which allows the metal to fill thin cross-sections; the minimum possible cross-section is . This results in a

near net shape Near-net-shape is an industrial manufacturing technique. As the name implies, the initial production of the item is very close to the final, or ''net'', shape. This reduces the need for surface finishing. By minimizing the use of finishing method ...

casting, which can be a cost advantage on complex parts. It also produces minimal scrap material. The major disadvantage of the process is that it can only be used with lower melting temperature non-ferrous materials, such as

aluminium Aluminium (aluminum in American and Canadian English) is a chemical element with the symbol Al and atomic number 13. Aluminium has a density lower than those of other common metals, at approximately one third that of steel. It ha ...

magnesium Magnesium is a chemical element with the symbol Mg and atomic number 12. It is a shiny gray metal having a low density, low melting point and high chemical reactivity. Like the other alkaline earth metals (group 2 of the periodic ...

zinc Zinc is a chemical element with the symbol Zn and atomic number 30. Zinc is a slightly brittle metal at room temperature and has a shiny-greyish appearance when oxidation is removed. It is the first element in group 12 (IIB) of the periodi ...

and sometimes copper alloys. The most commonly used material is aluminium. The maximum working temperature of plaster is , so higher melting temperature materials would melt the plaster mold. Also, the

sulfur Sulfur (or sulphur in British English) is a chemical element with the symbol S and atomic number 16. It is abundant, multivalent and nonmetallic. Under normal conditions, sulfur atoms form cyclic octatomic molecules with a chemical formul ...

in the gypsum reacts with iron, making it unsuitable for casting ferrous materials. Another disadvantage is that its long cooling times restrict production volume. Onetime molds are often quenched in water but only after completing solidification so hot metal does not fly everywhere. Proper quenching can aid in mold removal and it makes some alloys stronger. Plaster is not as stable as sand, so it is dependent on several factors, including the consistency of the plaster composition, pouring procedures, and curing techniques. If these factors are not closely monitored the mold can be distorted, shrink upon drying, have a poor surface finish, or fail completely..