Copper alloys are metal alloys that have copper as their principal component. They have high resistance against corrosion. The best known traditional types are bronze, where tin is a significant addition, and brass, using zinc instead. Both of these are imprecise terms, having both been commonly referred to as lattens in the past. Today the term ''copper alloy'' tends to be substituted, especially by museums. Composition The similarity in external appearance of the various alloys, along with the different combinations of elements used when making each alloy, can lead to confusion when categorizing the different compositions. There are as many as 400 different copper and copper alloy compositions loosely grouped into the categories: copper, high copper alloy, brasses, bronzes, copper nickels, copper–nickel–zinc (nickel silver), leaded copper, and special alloys. The following table lists the principal alloying element for four of the more common types used in mod ... [...More Info...] [...Related Items...] OR: [Wikipedia] [Google] [Baidu] |
Bronze
Bronze is an alloy consisting primarily of copper, commonly with about 12–12.5% tin and often with the addition of other metals (including aluminium, manganese, nickel, or zinc) and sometimes non-metals, such as phosphorus, or metalloids such as arsenic or silicon. These additions produce a range of alloys that may be harder than copper alone, or have other useful properties, such as strength, ductility, or machinability. The archaeological period in which bronze was the hardest metal in widespread use is known as the Bronze Age. The beginning of the Bronze Age in western Eurasia and India is conventionally dated to the mid-4th millennium BCE (~3500 BCE), and to the early 2nd millennium BCE in China; elsewhere it gradually spread across regions. The Bronze Age was followed by the Iron Age starting from about 1300 BCE and reaching most of Eurasia by about 500 BCE, although bronze continued to be much more widely used than it is in modern times. Because historical artworks w ... [...More Info...] [...Related Items...] OR: [Wikipedia] [Google] [Baidu] |
Copper Alloy
Copper alloys are metal alloys that have copper as their principal component. They have high resistance against corrosion. The best known traditional types are bronze, where tin is a significant addition, and brass, using zinc instead. Both of these are imprecise terms, having both been commonly referred to as lattens in the past. Today the term ''copper alloy'' tends to be substituted, especially by museums. Composition The similarity in external appearance of the various alloys, along with the different combinations of elements used when making each alloy, can lead to confusion when categorizing the different compositions. There are as many as 400 different copper and copper alloy compositions loosely grouped into the categories: copper, high copper alloy, brasses, bronzes, copper nickels, copper–nickel–zinc (nickel silver), leaded copper, and special alloys. The following table lists the principal alloying element for four of the more common types used in mod ... [...More Info...] [...Related Items...] OR: [Wikipedia] [Google] [Baidu] |
Leaded Copper
Leaded copper is a metal alloy of copper with lead. A small amount of lead makes the copper easier to machine. Alloys with a larger amount of lead are used for bearings. Brass and bronze alloys of copper may have lead added and are then also sometimes referred to as leaded copper alloys.Welter (2014) Leaded copper and its alloys have been used since ancient times. Applications Leaded copper alloys are used to make electrical connectors and mechanical bearings, especially in the automotive industry where high performance and reliability are required. Mechanical bearings can have high lead content. Such high lead content alloys are unsuitable for welding or brazing. Machined alloys Alloys with around 2-4% lead are used for machined copper applications, where the lead content lubricates the copper and makes it easier to machine. These include high-quality electrical connectors where a high current capacity and low electrical resistance are required. Such connectors are used in indust ... [...More Info...] [...Related Items...] OR: [Wikipedia] [Google] [Baidu] |
Binary Cu Sn Phase Diagram, Generated Using NIMS Open Database Cu-Sn And Computherm Pandat Https---computherm
Binary may refer to: Science and technology Mathematics * Binary number, a representation of numbers using only two digits (0 and 1) * Binary function, a function that takes two arguments * Binary operation, a mathematical operation that takes two arguments * Binary relation, a relation involving two elements * Binary-coded decimal, a method for encoding for decimal digits in binary sequences * Finger binary, a system for counting in binary numbers on the fingers of human hands Computing * Binary code, the digital representation of text and data * Bit, or binary digit, the basic unit of information in computers * Binary file, composed of something other than human-readable text ** Executable, a type of binary file that contains machine code for the computer to execute * Binary tree, a computer tree data structure in which each node has at most two children Astronomy * Binary star, a star system with two stars in it * Binary planet, two planetary bodies of comparable mas ... [...More Info...] [...Related Items...] OR: [Wikipedia] [Google] [Baidu] |
Cu Zn Phase Diagram
CU or cu, may refer to: * Close-up, in film making * Cuba (ISO 3166, FIPS Pub 10-4 and obsolete NATO digram) ** .cu, Cuba's top-level domain country code * Old Church Slavonic (ISO 639 alpha-2 language code) * "See you", in e-mail shorthand * Cubit, ancient unit of length Businesses and organizations * CU (store), a chain of South Korean convenience stores *Customs union, a type of intergovernmental trade bloc *ChristianUnion, a political party in the Netherlands *Christian Union (students), a university or college student Christian group *Consumers Union, a non-profit organization based in the United States *Credit union, a member-owned financial cooperative *Cubana de Aviación (IATA airline designator CU) Science, technology, and mathematics * Copper, symbol Cu, a chemical element * CU (power line), running between North Dakota and Minnesota, US * cu (Unix utility), a remote login command * Callous and unemotional traits, in psychology * Cellulase Unit, an enzyme meas ... [...More Info...] [...Related Items...] OR: [Wikipedia] [Google] [Baidu] |
Pounds Per Square Inch
The pound per square inch or, more accurately, pound-force per square inch (symbol: lbf/in2; abbreviation: psi) is a unit of pressure or of stress based on avoirdupois units. It is the pressure resulting from a force of one pound-force applied to an area of one square inch. In SI units, 1 psi is approximately equal to 6895 Pa. Pounds per square inch absolute (psia) is used to make it clear that the pressure is relative to a vacuum rather than the ambient atmospheric pressure. Since atmospheric pressure at sea level is around , this will be added to any pressure reading made in air at sea level. The converse is pounds per square inch gauge (psig), indicating that the pressure is relative to atmospheric pressure. For example, a bicycle tire pumped up to 65 psig in a local atmospheric pressure at sea level (14.7 psi) will have a pressure of 79.7 psia (14.7 psi + 65 psi). When gauge pressure is referenced to something other than ambient atmospheric pressure, then th ... [...More Info...] [...Related Items...] OR: [Wikipedia] [Google] [Baidu] |
Brinell Scale
The Brinell scale characterizes the indentation hardness of materials through the scale of penetration of an indenter, loaded on a material test-piece. It is one of several definitions of hardness in materials science. History Proposed by Swedish engineer Johan August Brinell in 1900, it was the first widely used and standardised hardness test in engineering and metallurgy. The large size of indentation and possible damage to test-piece limits its usefulness. However, it also had the useful feature that the hardness value divided by two gave the approximate UTS in ksi for steels. This feature contributed to its early adoption over competing hardness tests. Test details The typical test uses a diameter steel ball as an indenter with a force. For softer materials, a smaller force is used; for harder materials, a tungsten carbide ball is substituted for the steel ball. The indentation is measured and hardness calculated as: :\operatorname=\frac where: :BHN = Brinell Hardn ... [...More Info...] [...Related Items...] OR: [Wikipedia] [Google] [Baidu] |
ASTM International
ASTM International, formerly known as American Society for Testing and Materials, is an international standards organization that develops and publishes voluntary consensus technical standards for a wide range of materials, products, systems, and services. Some 12,575 ASTM voluntary consensus standards operate globally. The organization's headquarters is in West Conshohocken, Pennsylvania, about northwest of Philadelphia. It is founded in 1902 as the American Section of the International Association for Testing Materials (see also International Organization for Standardization). History A group of scientists and engineers, led by Charles Dudley, formed ASTM in 1898 to address the frequent rail breaks affecting the fast-growing railroad industry. The group developed a standard for the steel used to fabricate rails. Originally called the "American Society for Testing Materials" in 1902, it became the "American Society for Testing And Materials" in 1961. In 2001, ASTM off ... [...More Info...] [...Related Items...] OR: [Wikipedia] [Google] [Baidu] |
Gilding Metal
Gilding metal is a form of brass (an alloy of copper and zinc) with a much higher copper content than zinc content. Exact figures range from 95% copper and 5% zinc to “8 parts copper to 1 of zinc” (11% zinc) in British Army Dress Regulations. Gilding metal is used for various purposes, including the jackets of bullets, driving bands on some artillery shells, as well as enameled badges and other jewellery. The sheet is widely used for craft metalworking by hammer working. It is also used particularly as a lower-cost training material for silversmiths. Starting in 1944, shell casings made of gilding metal were melted down by the United States Mint to be made into pennies. These pennies replaced the less popular steel cent of 1943, and the pennies of this composition were produced until 1946. Gilding metal was also used for the "bronze" Olympic medal at the 2020 Summer Olympics held in Tokyo, Japan in 2021. Gilding metal may be annealed by heating to between . It should b ... [...More Info...] [...Related Items...] OR: [Wikipedia] [Google] [Baidu] |
Section 23 2D CU-SI
Section, Sectioning or Sectioned may refer to: Arts, entertainment and media * Section (music), a complete, but not independent, musical idea * Section (typography), a subdivision, especially of a chapter, in books and documents ** Section sign (§), typographical characters * Section (bookbinding), a group of sheets, folded in the middle, bound into the binding together * The Section (band), a 1970s American instrumental rock band * ''The Outpost'' (1995 film), also known as ''The Section'' * Section, an instrumental group within an orchestra * "Section", a song by 2 Chainz from the 2016 album ''ColleGrove'' * "Sectioning", a ''Peep Show'' episode * David "Section" Mason, a fictional character in '' Call of Duty: Black Ops II'' Organisations * Section (Alpine club) * Section (military unit) * Section (Scouting) Science, technology and mathematics Science * Section (archaeology), a view in part of the archaeological sequence showing it in the vertical plane * Section (bi ... [...More Info...] [...Related Items...] OR: [Wikipedia] [Google] [Baidu] |
Bullet
A bullet is a kinetic projectile, a component of firearm ammunition that is shot from a gun barrel. Bullets are made of a variety of materials, such as copper, lead, steel, polymer, rubber and even wax. Bullets are made in various shapes and constructions (depending on the intended applications), including specialized functions such as hunting, target shooting, training and combat. Bullets are often tapered, making them more aerodynamic. Bullet sizes are expressed by their weights and diameters (referred to as "calibers") in both imperial and metric measurement systems. For example: 55 grain .223 caliber bullets are of the same weight and caliber as 3.56 gram 5.56mm caliber bullets. Bullets do not normally contain explosives but strike or damage the intended target by transferring kinetic energy upon impact and penetration. Bullets shot by firearms can be used for target practice or hunting. Description The term ''bullet'' is from Middle French, originating as the diminutiv ... [...More Info...] [...Related Items...] OR: [Wikipedia] [Google] [Baidu] |