The term hardened steel is often used for a medium or high carbon
steel Steel is an alloy made up of iron with added carbon to improve its strength and fracture resistance compared to other forms of iron. Many other elements may be present or added. Stainless steels that are corrosion- and oxidation-resistan ...
that has been given heat treatment and then
quenching In materials science, quenching is the rapid cooling of a workpiece in water, oil, polymer, air, or other fluids to obtain certain material properties. A type of heat treating, quenching prevents undesired low-temperature processes, such as ...
followed by tempering. The quenching results in the formation of metastable
martensite Martensite is a very hard form of steel crystalline structure. It is named after German metallurgist Adolf Martens. By analogy the term can also refer to any crystal structure that is formed by diffusionless transformation. Properties M ...
, the fraction of which is reduced to the desired amount during tempering. This is the most common state for finished articles such as tools and machine parts. In contrast, the same steel composition in annealed state is softer, as required for forming and
machining Machining is a process in which a material (often metal) is cut to a desired final shape and size by a controlled material-removal process. The processes that have this common theme are collectively called subtractive manufacturing, which utilizes ...
. Depending on the temperature and composition of the steel, it can be hardened or softened. To make steel harder, it must be heated to very high temperatures. The final result of exactly how hard the steel becomes depends on the amount of carbon present in the metal. Only steel that is high in carbon can be hardened and tempered. If a metal does not contain the necessary quantity of carbon, then its crystalline structure cannot be broken, and therefore the physical makeup of the steel cannot be altered. Frequently, the term "hardening" is associated with tempered steel. Both processes are used hand in hand when hardening steel. The two part process begins with hardening the steel so that it becomes hard and does not wear over time. However, very often, this process leaves the steel very brittle and susceptible to breaking during use. Tempering reduces the hardness of the forged steel very slightly but improves the overall product as it results in steel that is much less brittle.


Hardening and tempering

The two major processes of hardening and tempering can be broken down into four major steps. First, a piece of carbon steel is heated gradually until it reaches a temperature above the alloy's critical temperature. The steel is then quenched, usually in water or oil (though other quenches, such as brine or sodium hydroxide solutions, are sometimes used to achieve a particular result). The steel is now at that given alloy's maximum hardness, but as stated above, also brittle. At this point, tempering is usually performed to achieve a more useful balance of hardness and toughness. The steel is gradually heated until the desired temper colours are drawn, generally at a temperature significantly lower than the alloy's critical temperature. Different colours in the temper spectrum reflect different balances of hardness to toughness, so different temper levels are appropriate for different applications. The steel is then re-quenched to 'fix' the temper at the desired level. A talented smith or metalworker can fine-tune the performance of a steel tool or item to precisely what is required based solely on careful observation of temper colours.
visual representation
of this process may make the concept easier to understand.


Testing for hardened steel

It is not easy to determine if steel has undergone the hardening and tempering process by simply looking at it, but there is a reliable and simple test. To examine a piece of steel, obtain a hand file and file an edge of the selected metal. If the piece of steel has not undergone the hardening process, the metal file should easily 'bite' into the sample. If the metal has been hardened, the file fails to cut into the sample and glances off with little visible effect.
Case hardened Case-hardening or surface hardening is the process of hardening the surface of a metal object while allowing the metal deeper underneath to remain soft, thus forming a thin layer of harder metal at the surface. For iron or steel with low carbon ...
articles starting as low carbon steel (0.5 - 1.5% carbon content) can also be labeled hardened steel.