LiCoO2

Lithium cobalt oxide, sometimes called lithium cobaltateA. L. Emelina, M. A. Bykov, M. L. Kovba, B. M. Senyavin, E. V. Golubina (2011), "Thermochemical properties of lithium cobaltate". ''Russian Journal of Physical Chemistry'', volume 85, issue 3, pages 357–363; or lithium cobaltite,Ondřej Jankovský, Jan Kovařík, Jindřich Leitner, Květoslav Růžička, David Sedmidubský (2016) "Thermodynamic properties of stoichiometric lithium cobaltite LiCoO2". ''Thermochimica Acta'',
volume 634, pages 26-30. is a chemical compound with formula . The cobalt atoms are formally in the +3 oxidation state, hence the IUPAC name lithium cobalt(III) oxide.

Lithium cobalt oxide is a dark blue or bluish-gray crystalline solid,LinYi Gelon New Battery Materials Co., Ltd
"Lithium Cobalt Oxide (LiCoO2) for lithium ion battery "
Catalog entry, accessed on 2018-04-10, and is commonly used in the positive electrodes of lithium-ion batteries especially in handheld electronics.

Structure

The structure of has been studied with numerous techniques including x-ray diffraction, electron microscopy, neutron powder diffraction, and EXAFS.

The solid consists of layers of monovalent lithium cations () that lie between extended anionic sheets of cobalt and oxygen atoms, arranged as edge-sharing octahedra, with two faces parallel to the sheet plane. The cobalt atoms are formally in the trivalent oxidation state () and are sandwiched between two layers of oxygen atoms ().

In each layer (cobalt, oxygen, or lithium), the atoms are arranged in a regular triangular lattice. The lattices are offset so that the lithium atoms are farthest from the cobalt atoms, and the structure repeats in the direction perpendicular to the planes every three cobalt (or lithium) layers. The point group symmetry is $R\bar 3m$ in Hermann-Mauguin notation, signifying a unit cell with threefold improper rotational symmetry and a mirror plane. The threefold rotational axis (which is normal to the layers) is termed improper because the triangles of oxygen (being on opposite sides of each octahedron) are anti-aligned.

Preparation

Fully reduced lithium cobalt oxide can be prepared by heating a stoichiometric mixture of lithium carbonate and cobalt(II,III) oxide or metallic cobalt at 600–800 °C, then annealing the product at 900 °C for many hours, all under an oxygen atmosphere.

Nanometer-size particles more suitable for cathode use can also be obtained by calcination of hydrated cobalt oxalate β-·2, in the form of rod-like crystals about 8 μm long and 0.4 μm wide, with lithium hydroxide , up to 750–900 °C.

A third method uses lithium acetate, cobalt acetate, and citric acid in equal molar amounts, in water solution. Heating at 80 °C turns the mixture into a viscous transparent gel. The dried gel is then ground and heated gradually to 550 °C.

Use in rechargeable batteries

The usefulness of lithium cobalt oxide as an intercalation electrode was discovered in 1980 by an Oxford University research group led by John B. Goodenough and Tokyo University's Koichi Mizushima.

The compound is now used as the cathode in some rechargeable lithium-ion batteries, with particle sizes ranging from nanometers to micrometers. During charging, the cobalt is partially oxidized to the +4 state, with some lithium ions moving to the electrolyte, resulting in a range of compounds with 0 < ''x'' < 1.

Batteries produced with cathodes have very stable capacities, but have lower capacities and power than those with cathodes based on (especially nickel-rich) nickel-cobalt-aluminum (NCA) or nickel-cobalt-manganese (NCM) oxides. Issues with thermostability are better for cathodes than other nickel-rich chemistries although not significantly. This makes batteries susceptible to thermal runaway in cases of abuse such as high temperature operation (>130 °C) or overcharging. At elevated temperatures, decomposition generates oxygen, which then reacts with the organic electrolyte of the cell, this reaction is often seen in Lithium-Ion batteries where the battery becomes highly volatile and must be recycled in a safe manner. The decomposition of LiCoO₂ is a safety concern due to the magnitude of this highly exothermic reaction, which can spread to adjacent cells or ignite nearby combustible material. In general, this is seen for many lithium-ion battery cathodes.

The delithiation process is usually by chemical means, although a novel physical process has been developed based on ion sputtering and annealing cycles, leaving the material properties intact.

See also

* List of battery types
* Sodium cobalt oxide

References

External links

Imaging the Structure of Lithium Cobalt Oxide at Atomic Level
from the Lawrence Berkeley National Laboratory

{{Cobalt compounds

Cobalt(III) compounds
Lithium compounds
Oxides